Evaluation of the Sealing Ability of Direct versus Direct-Indirect Veneer Techniques: An In Vitro Study
Mewan Salahalddin Abdulrahman1
1University of Sulaimani, College of Dentistry, Kurdistan Region, Iraq.
Backgrounds:
Marginal discoloration, microleakage, wear, and marginal fractures are all prevalent problems with composite veneers, and this scenario leads the esthetic outcome to deteriorate with time, resulting in patient discontent. Aim of the Study. The study's goal was to determine the marginal sealing ability of composite laminate veneers when employing two types of veneer techniques: direct and direct-indirect veneers, as well as two types of composite resin: nanohybrid and microfilled composite resin restorations, using dye penetration method.
Materials And Methods:
In this study, forty extracted human teeth were utilized. Following a standardized veneer preparation on the labial surface of the teeth, they were separated into two groups of 20 teeth each, using the following composite application techniques: group A: direct veneers and group B: direct-indirect veneers. Following that, each major group was separated into two subgroups of ten teeth each, based on the type of composite employed: subgroup 1 used nanohybrid composite resin, while subgroup 2 used microfilled composite resin. All of the samples were kept in distilled water, thermocycled, and soaked in 2% basic fuchsine dye. These specimens were sectioned and examined under a stereomicroscope for dye penetration at the gingival margin. The data was analyzed using independent T-tests using SPSS 22.
Result:
Using direct-indirect veneer technique with nanohybrid composite resin material resulted in the most negligible dye penetration at the gingival margin, while using direct veneer technique with microfilled composite resin material resulted in the maximum dye penetration. For both composite materials, gingival microleakage was lower when using the direct-indirect veneer technique than when using the direct technique, and the difference was statistically significant (P < 0.05). In both techniques, gingival microleakage was lower with nanohybrid composite than with microfilled composite, and the difference was statistically highly significant (P = 0.001).
Conclusion:
The sealing ability of the gingival margin of tooth/composite interface is better when applying direct-indirect veneer technique with nanohybrid composite resin than that of direct veneer technique with microfilled composite resin material.