Transition from spin glass to paramagnetism in the magnetic properties of PrAu₂Si₂

It is unexpected that a spin-glass (SG) transition, which generally occurs only in systems with some form of disorder, was observed in the ThCr₂Si₂-type compound PrAu₂Si₂at a temperature of ∼3 K. This puzzling phenomenon was later explained based on a novel dynamic frustration model that does not involve static disorder. We present the results of re-verification of the reported SG behaviors by measuring the physical properties of three polycrystalline PrAu₂Si₂samples annealed under different conditions. Indeed, in the sample annealed at 827 °C for one week, a SG transition does occur at a temperature ofT_f∼ 2.8 K as that reported previously in the literature. However, it is newly found that the SG effect is actually more pronounced in the as-cast sample, and almost completely disappears in the well-annealed (at 850 °C for four weeks) sample. The annealing effect observed in PrAu₂Si₂, that is, SG to paramagnetism transition is discussed by comparing with earlier results reported on the same system and other isomorphic compounds.