Deterioration Mechanisms and Advanced Inspection Technologies of Aluminum Windows

Huaguo Chen1, Cheuk Lun Chow1, Denvid Lau1

  • 1Department of Architecture and Civil Engineering, City University of Hong Kong, Hong Kong, China.

Materials (Basel, Switzerland)
|January 11, 2022
PubMed

Keywords:
aluminum windowsartificial intelligencedeterioration mechanismsenvironmental factorsinspection techniquesmolecular dynamics simulation

More Related Videos

Mechanoluminescent Visualization of Crack Propagation for Joint Evaluation04:58

Mechanoluminescent Visualization of Crack Propagation for Joint Evaluation

Published on: January 6, 2023

2.7K
In Situ Monitoring of the Accelerated Performance Degradation of Solar Cells and Modules: A Case Study for CuIn,GaSe2 Solar Cells09:19

In Situ Monitoring of the Accelerated Performance Degradation of Solar Cells and Modules: A Case Study for CuIn,GaSe2 Solar Cells

Published on: October 3, 2018

8.5K

Related Concept Videos

Mortar Joint Deterioration in Masonry01:13

Mortar Joint Deterioration in Masonry

Mortar joint deterioration is a significant concern in masonry structures, with water accumulation in the joints leading to damage from freeze-thaw cycles. The repeated expansion of water during freezing and its melting during thawing develop and propagate cracks in the masonry joints. Eventually, this leads to the spalling of mortar from the joints, loosening masonry units and weakening the structure. The deteriorated mortar joints are also vulnerable to moisture intrusion into the walls.
The...
174
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
231
Lumber Defects01:23

Lumber Defects

Lumber defects, which can affect both the appearance and structural integrity of wood, include a variety of growth and manufacturing flaws. Growth defects such as knots and knotholes occur where branches were once attached to the tree trunk, with knotholes forming when these knots fall out. Other natural defects include decay and insect damage, which compromise the wood's strength and durability.
Shakes are minor fractures that run along or across the wood's annual rings, while wane is...
246
Cavity Drainage and Flashings in Masonry walls01:20

Cavity Drainage and Flashings in Masonry walls

Typically, a cavity wall consists of two wythes separated by a gap of at least 2 inches, which may contain insulation while still maintaining a minimum clear space of 1 inch to facilitate adequate drainage. Advanced methods like the insertion of a continuous drainage mat can further reduce this space while ensuring effective moisture expulsion.
Weep holes, strategically placed at the base of the cavity, are critical for draining accumulated water. These openings are created by leaving head...
180
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
288