Enhanced Biocorrosion Resistance and Cellular Response of a Dual-Phase High Entropy Alloy through Reduced Elemental
Gopinath Perumal1, Harpreet Singh Grewal1, Mayur Pole2
1Department of Mechanical Engineering, School of Engineering, Shiv Nadar University, Greater Noida, Uttar Pradesh 201314, India.
Abstract:
The leaching out of toxic elements from metallic bioimplants has serious repercussions, including allergies, peripheral neuritis, cancer, and Alzheimer's disease, leading to revision or replacement surgeries. The development of advanced structural materials with excellent biocompatibility and superior corrosion resistance in the physiological environment holds great significance. High entropy alloys (HEAs) with a huge compositional design space and outstanding mechanical and functional properties can be promising for bioimplant applications. However, microstructural heterogeneity arising from elemental segregation in these multiprinciple alloy systems is the Achilles heel in the development of next-generation HEAs. Here, we demonstrate a pathway to homogenize the microstructure of a biocompatible dual-phase HEA, comprising refractory elements, namely, MoNbTaTiZr, through severe surface deformation using stationary friction processing (SFP). The strain and temperature field during processing homogenized the elemental distribution, which was otherwise unresponsive to conventional annealing treatments. Nearly 15 min of the SFP treatment resulted in a significant elemental homogenization across dendritic and interdendritic regions, similar to a week-long annealing treatment at 1275 K. The SFP processed alloy showed a nearly six times higher biocorrosion resistance compared to its as-cast counterpart. X-ray photoelectron spectroscopy was used to investigate the nature of the oxide layer formed on the specimens. Superior corrosion behavior of the processed alloy was attributed to the formation of a stable passive layer with zirconium oxide as the primary constituent and higher hydrophobicity. Biocompatibility studies performed using the human mesenchymal stem cell line, showed higher viability for the processed HEA compared to its as-cast counterpart as well as conventional metallic biomaterials including stainless steel (SS316L) and titanium alloy (Ti6Al4V).