Construction of Cu-BTC by carboxylic acid organic ligand and its application in low temperature SCR denitration

The removal of NO has always been a hot issue in the treatment of coal-fired flue gas. In this paper, a hydrothermal synthesis method was used to prepare porous denitration catalysts with polycarboxyl organic isomers (trimellitic acid, phthalic acid, and benzoic acid). And then developed as the NO removing catalysts for low temperature selective catalytic reduction (SCR) with NH₃. XRD, BET, SEM, FTIR, XPS, Raman, H₂-TPR, NH₃-TPD and TG were used to analyze the crystallinity, microscopic morphology, surface functional groups and metal content. The results showed that: (1) From the crystal structure analysis, the catalyst prepared with 1,3,5 and 1,2,4-benzenetricarboxylic acid as ligands (1,3,5-A and 1,2,4-B) was Cu-BTC. (2) 1,3,5-A catalyst had a huge specific surface area, up to 1421.32 m²/g, and a pore volume up to 0.5798 cm³/g. (3) The prepared catalysts were applied to NH₃-SCR denitration, and the catalyst with Cu-BTC structure had relatively high catalytic performance, and the overall catalytic capacity showed an increasing trend with the temperature. (4) 1,3,5-A catalyst had stability and catalytic activity. When the temperature was 270 °C, the denitration efficiency reached 83.87%. And within 8 h, the denitration efficiency was stable up to 82%.