Comparative effects on acrylic resin properties of short- and long-term immersion in alkaline peroxide solution

To evaluate the color stability (ΔE), surface roughness (ΔRa), and flexural strength of denture base acrylic resin after short (20 minutes) and long-term (8 hours) immersions simulating a period of 5 years of use.

120 disk-shaped (16 mm x 4 mm) and 120 rectangular (65 mm x 10 mm x 3.3 mm) specimens were prepared (Lucitone 550) and distributed into three groups (n=20): distilled water (Control); Corega Tabs (CT) and Polident (Po), for immersions of 20 minutes and 8 hours. ΔE were determined by a colorimeter, ΔRa by a profilometer and the flexural strength by a universal testing machine. Data were evaluated by two-way ANOVA followed by Tukey's test and Bonferroni correction (α= 0.05).

Short-term immersions for 20 minutes resulted in significant differences in ΔE, as CT values (1.46 ± 1.41) were higher than Po (0.55 ± 0.25) and Control (0.47 ± 0.21). Specimens immersed for 8 hours showed more extensive alterations overall than the control (ΔE [Po: 7.27 ± 0.53; CT: 5.58 ± 0.49; Control: 1.26 ± 0.23]; 916;Ra [Po: 0.16 ± 0.08; CT: 0.12 ± 0.11; Control: 0.07 ± 0.06]; flexural strength [Po: 42.99 ± 9.34; CT: 63.96 ± 12.98; Control: 64.59 ± 12.87]). The tested alkaline peroxide-based solutions promoted significant alteration on acrylic resin properties after overnight immersion. Therefore, short-term immersions seem to be more suitable for daily denture hygiene.

Alkaline peroxides were able to alter color stability, surface roughness and flexural strength of acrylic resin after overnight immersions, in a 5-year-simulated period of use.