Performance Improvement of Gold Electrode towards Methanol Electrooxidation in Akaline Medium: Enhanced Current...

Electronically conducting poly (aniline-co-2-hydroxyaniline) (PACHA), a copolymer of aniline and 2-hydroxyaniline (2HA), was electrochemically coated on gold substrate for methanol electrooxidation in alkaline media. The electrochemical behavior of PACHA coated gold electrode towards methanol electrooxidation was investigated via cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) for application in an alkaline fuel cell. Methanol electrooxidation was observed at two different electrode potentials depending on the concentration of the base. At the PACHA coated gold electrode, the methanol oxidation peak was observed at lower overpotential (at 0.19 V) in a solution of high base concentration (1.8 M NaOH), which was 30 mV lower than the peak for the uncoated gold electrode. In addition, the Faradic current Imax obtained on the PACHA coated electrode (20 mA) was two times higher as compared to the Faradic current Imax of the un-modified gold electrode (10 mA). In solution of lower base concentration (0.06 M NaOH), the electrooxidation of methanol became sluggish on both electrodes, as indicated by peak shifting towards positive potential and with reduced faradaic current (at 0.74 V on PACHA coated electrode; Imax 10 mA). The electrooxidation of methanol at both lower and higher electrode potentials was analyzed mechanistically and discussed in light of the literature. EIS results were interpreted using Nyquist and Bode plots. The charge transfer resistance was decreased and pseudo-capacitive behavior changed to conductive behavior when external applied potential was increased from 0.1 V to 0.4 V.