Microleakage beneath orthodontic brackets in high field magnetic resonance imaging (MRI) AT 1.5 & 3 Tesla

The aim of the present study was to evaluate the effects of 1.5 T and 3 T MRI on the adhesion between the orthodontic brackets and the teeth by evaluating the microleakage between the enamel, adhesive and brackets interfaces.

58 extracted human premolars which were received a standard bracket bonding procedure were randomly divided into three groups; control group (n = 20; no MRI), 1.5 T MRI group (n = 19; 20 min MRI exposure of 1.5 T) and 3 T MRI group (n = 19; 20 min MRI exposure of 3 T). The teeth were kept in distiled water for 2 weeks, and thereafter subjected to 500 thermal cycles. Then, specimens were sealed with nail varnish, stained with 0.5% basic fuchsin for 24 h, sectioned and photographed under a stereomicroscope. Microleakage was scored with regard to the adhesive-enamel and bracket-adhesive interfaces at the occlusal and gingival levels. Statistical analysis was accomplished by Kruskal-Wallis and Bonferroni-Dunn tests.

All of the groups exhibited statistically similar microleakage scores in the adhesive-enamel interface along occlusal margins (p>0.05, p = 0.331). The mean microleakage scores along gingival margins in the 3 T MRI group was significantly higher compared to the control group both in the adhesive-enamel and bracket-adhesive interfaces (p<0.05, p = 0.019 and p = 0.020 respectively). The microleakage scores along the gingival margins were also significantly higher than the occlusal margins in the 3 T MRI group (p<0.05, p = 0.029).

3 T MRI may weaken the adhesion between the enamel and the stainless steel orthodontic brackets.