Synthesis and characterization of polystyrene with embedded silver nanoparticle nanofibers to utilize as
Mayar Mostafa1, Nadia G Kandile1, Mahmoud K Mahmoud2
1Chemistry Department, Faculty of Women for Arts, Science and Education, Ain Shams University, Heliopolis, 11757, Cairo, Egypt.
Abstract:
Herein, silver nanoparticles (Ag) embedded in polystyrene (PS) nanofiber composites have been prepared by an electrospinning technique using N, N-dimethylformamide (DMF) as a solvent and safe reducing agent. Electrospinning of polystyrene (PS) solutions is conducted using different electrospinning parameters such as polymer concentration in the electrospinning solution; solution feed rate, and electrical field strength. Then silver nanoparticles (AgNPs) were embedded into PS nanofibers to obtain an AgNPs-PS nanofiber composite as a powerful, cheap, and nontoxic bioactive material. PS nanofibers and AgNPs-PS nanofibers composite were characterized by using thermogravimetric analysis (TGA), X-ray diffraction, and scanning electron microscopy (SEM). Also, AgNPs were characterized by UV-vis spectroscopy, transmission electron microscopy (TEM), and EDX analysis. Results showed that PS nanofibers were obtained with concentrations ranging from 10-30 wt.% in DMF solvent. Also, an AgNPs-PS nanofiber composite has been produced from its solutions by using DMF at the optimum value. The prepared AgNPs have a 21-40 nm particle size and a semi-spherical shape. In addition, the antibacterial activity of AgNPs-PS nanofibers towards both Gram-positive and Gram-negative bacteria has been increased. Therefore, this nanocomposite can be used as a powerful bioactive material in biomedical fields.