Nanofibrillated cellulose/glucosamine 3D aerogel implants loaded with rosuvastatin and bioactive ceramic for dental...

Recycling of agro-wastes presents a great economic and ecologic value. In this study, TEMPO-oxidized nanofibrillated cellulose (TONFC) originating from sugarcane bagasse pulp was exploited in regenerative medicine. TONFC in combination with glucosamine HCl (G) were used to prepare a 3D aerogel implant loaded with rosuvastatin as an integrative approach for extraction-socket healing. Comparing the prepared devices, aerogel composed of TONFC: G (4:1 wt ratio) had the best mechanical properties and integrity. Strontium borate-based bioactive ceramic particles were prepared and characterized for crystal structure, shape, porosity, and zeta potential. The particles had a crystalline diffraction pattern relative to Sr₃B₂O₆, and they were rod in shape with nanopores with a zeta potential value of -16 mV. The prepared bioactive ceramic (BC) was then added in different concentrations (3 or 6% w/w) to the selected aerogel implant. The BC had a concentration-dependent effect on the aerogel properties as it ameliorated its mechanical performance (compressive strength = 90 and 150 kPa for 3 and 6%, respectively) and retarded drug release (mean release time = 2.34 and 3.4 h for 3 and 6%, respectively) (p < 0.05). The microphotograph of the selected aerogel implant loaded with BC showed a rough surface with an interconnective porous structure. During cell biology testing, the selected implant loaded with the lower BC concentration had the highest ability to increase MG-63 cells proliferation. In conclusion, TONFC is a promising material to formulate rosuvastatin-loaded aerogel implant with the aid of glucosamine and bioactive ceramic for dental socket preservation.