Environment-friendly degradable zinc-ion battery based on guar gum-cellulose aerogel electrolyte

With the vigorous development of electronics and the increasingly prominent problem of environmental pollution, it is particularly important to exploit environmentally friendly electronic devices. Transient electronics represent a kind of device that once the specified functions have completed can completely or partially disappear through physical or chemical actions. In this work, we introduce a novel guar gum-cellulose aerogel (GCA) membrane based on natural biomaterials and successfully use it as an electrolyte film to fabricate a degradable zinc-ion battery (DZIB). All components of the prepared DZIBs can be successfully degraded or disintegrate in phosphate-buffered saline (PBS) containing a solution of proteinase K after approximately 40 days. This electrolyte film has a high ionic conductivity of approximately 4.73 × 10^-2 S cm^-1 and a good mechanical stress property. When applied to DZIB, the production of zinc dendrites can be restrained, leading to the battery showing excellent electrochemical performance. The battery exhibits a specific capacity of 309.1 mA h g^-1 at a current density of 308 mA g^-1 after 100 cycles and a steady cycling ability (100% capacity retention after 200 cycles). More importantly, the electrochemical performance of DZIB is better than that of transient batteries reported in the past, taking a solid step in the field of transient electronics in the initial stage.