Effect of Process Temperature on Density and Electrical Characteristics of Hf_0.5Zr_0.5O₂ Thin Films Prepared by...

HfZr_1-O₂ (HZO) thin films have excellent potential for application in various devices, including ferroelectric transistors and semiconductor memories. However, such applications are hindered by the low remanent polarization (P_r) and fatigue endurance of these films. To overcome these limitations, in this study, HZO thin films were fabricated via plasma-enhanced atomic layer deposition (PEALD), and the effects of the deposition and post-annealing temperatures on the density, crystallinity, and electrical properties of the thin films were analyzed. The thin films obtained via PEALD were characterized using cross-sectional transmission electron microscopy images and energy-dispersive spectroscopy analysis. An HZO thin film deposited at 180 °C exhibited the highest o-phase proportion as well as the highest density. By contrast, mixed secondary phases were observed in a thin film deposited at 280 °C. Furthermore, a post-annealing temperature of 600 °C yielded the highest thin film density, and the highest 2P_r value and fatigue endurance were obtained for the film deposited at 180 °C and post-annealed at 600 °C. In addition, we developed three different methods to further enhance the density of the films. Consequently, an enhanced maximum density and exceptional fatigue endurance of 2.5 × 10⁷ cycles were obtained.