A New System for Periprosthetic Fracture Stabilization-A Biomechanical Comparison

In recent years, an increase in periprosthetic femur fractures has become apparent due to the increased number of hip replacements. In the case of Vancouver type B1 fractures, locking plate systems offer safe procedures. This study compared the distal lateral femur plate (LOQTEQ^®, aap Implantate AG) with a standard L.I.S.S. LCP^® (DePuy Synthes) regarding their biomechanical properties in fixation of periprosthetic femur fractures after hip arthroplasty. We hypothesized that the new LOQTEQ system has superior stability and durability in comparison. Eighteen artificial left femurs were randomized in two groups (Group A: LOQTEQ^®; Group B: L.I.S.S. LCP^®) and tested until failure. Failure was defined as 10° varus deformity and catastrophic implant failure (loosening, breakage, progressive bending). Axial stiffness, loads of failure, cycles of failure, modes of failure were recorded. The axial stiffness in Group A with 73.4 N/mm (SD +/- 3.0) was significantly higher (p = 0.001) than in Group B (40.7 N/mm (SD +/- 2.8)). Group A resists more cycles than Group B until 10° varus deformity. Catastrophic failure mode was plate breakage in Group A and bending in Group B. In conclusion, LOQTEQ^® provides higher primary stability and tends to have higher durability.