The Effects of Cooling and Shrinkage on the Life of Polymer 3D Printed Injection Moulds

Anurag Bagalkot1, Dirk Pons1, Digby Symons1

  • 1Department of Mechanical Engineering, University of Canterbury, Private Bag 4800, Christchurch 8020, New Zealand.

Polymers
|February 15, 2022
PubMed

Keywords:
additive manufacturingcooling timeejection failureinjection mouldingrapid toolingtool failure

More Related Videos

A Soft Tooling Process Chain for Injection Molding of a 3D Component with Micro Pillars05:32

A Soft Tooling Process Chain for Injection Molding of a 3D Component with Micro Pillars

Published on: August 4, 2018

12.8K
Author Spotlight: Modular Neuronal Networks for Analyzing Brain Functions07:38

Author Spotlight: Modular Neuronal Networks for Analyzing Brain Functions

Published on: June 7, 2024

1.8K

Related Concept Videos

Drying Shrinkage01:21

Drying Shrinkage

When hardened concrete is exposed to air with a relative humidity of less than 100 percent, it begins to lose the free water within its capillaries. As this water evaporates, the water initially adsorbed onto the calcium silicate hydrates migrates towards these now empty spaces and eventually evaporates as well. Over time, as more water leaves, the volume of the concrete decreases, a phenomenon known as drying shrinkage.
A portion of this drying shrinkage can be reversed; if the concrete is...
173
Shrinkage in Concrete01:27

Shrinkage in Concrete

Shrinkage in concrete is primarily due to water loss from evaporation, hydration of cement, or carbonation, leading to a reduction in volume. The volumetric contraction results in volumetric strain in concrete. However, in practice, shrinkage is measured as linear strain, which is one-third of the volumetric strain.
When concrete is still in its plastic state, it can undergo a decrease in volume by about 1% of its absolute volume. This decrease is known as plastic shrinkage. It arises either...
185
Residual Stresses01:26

Residual Stresses

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...
304
Carbonation Shrinkage01:24

Carbonation Shrinkage

Atmospheric CO2 penetrates the concrete's pores and, in the presence of moisture, forms carbonic acid, which then reacts with calcium hydroxide in the hydrated cement, forming calcium carbonate. This process reduces the concrete's volume and is termed carbonation shrinkage.
The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
237
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and...