Structural Changes in Resin-Based Composites in Saliva of Patients with Leukemia before Starting Chemotherapeutic...

Background: The aim of this in vitro study was to assess the morphological characteristics and stability of dental composites immersed in saliva collected from patients with leukemia. Material and Methods: A total number of five patients without systemic disease and 20 patients with leukemia (acute lymphoblastic leukemia (ALL), acute myeloid leukemia (AML), chronic lymphocytic leukemia (CLL), and chronic myeloid leukemia (CML)) were included for saliva sampling. Composite disks were immersed in the leukemia, control, and artificial environments for 7 days. At the end of the experiment, atomic force microscopy (AFM), color stability (ΔE), and saliva elements analysis were performed. Statistical significance was considered for a p-value under 0.05. Results: The most changed surface resulted for ALL with a roughness that was almost double that of the untreated sample and was significantly increased compared to the healthy saliva. The effect of CLL was not as intense as observed for acute leukemia, but was significantly over the control. ALL seemed to modify structural components of the saliva, which were able to deteriorate the surface of the composite. ALL saliva promoted a significant dissolution of the initial feature of the samples and promoted nano-particle clusterization. All dental composites showed clinically acceptable color change values (ΔE < 3.3) in all four-leukemia salivas; CLL and CML showed large color differences for all composites. The total concentrations of P, Na, and K showed wide ranges of variations, while the coefficient of variation in Fe, Cu, and Mg showed narrow variations between the salvias' investigated. The salivary concentration of zinc decreased considerably in the CLL and CML environments compared to the ALL and AML environments. Fe and Cu were significantly increased in the CML environment. Conclusions: Control and artificial salivas have a mild erosive effect on the surface of dental composites. The acute stage of the disease seems to deteriorate the surface roughness rather than its morphology, however, in the chronic stage, it is the surface morphology that mostly deteriorates.