Chitosan/sodium polyborate based micro-nano coating with high flame retardancy and superhydrophobicity for cotton
Peng Qi1, Shuheng Wang1, Wenjia Wang1
1State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, PR China; Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing, 100029, PR China.
Abstract:
In this work, a sustainable flame retardant and superhydrophobic cotton fabric was prepared by a two-step process: the cotton fabric was firstly treated with a chitosan/sodium polyborate polyelectrolyte complex water solution to obtain a flame retardant layer, and then treated with a polydimethylsiloxane (PDMS) tetrahydrofuran solution to construct a superhydrophobic layer. The phase-separated chitosan with a micro-nano roughness structure was covered by PDMS, which synergistically improved the hydrophobicity of the cotton fabric. The flammability evaluation indicated that the limiting oxygen index value of the treated fabric was increased to 40.0% from 18.2%, the peak of heat release rate was reduced by 63.8%, and the total heat release was reduced by 57.6% compared with that of the control sample. The enhanced flame retardancy was attributed to the excellent charring ability in the condensed phase. The treated fabric also showed anti-sticking, self-cleaning, and oil/water-separating properties. This coating treatment without any F, Cl, Br, P elements involved is regarded as a clean methodology for producing flame retardant and superhydrophobic cotton fabrics.