Synthesis of silver nanoparticles by sonogalvanic replacement on aluminium powder in sodium polyacrylate solutions

The process of the formation of silver nanoparticles (AgNPs) via the method of galvanic replacement (GR) of Ag⁺ with aluminum powder in sodium polyacrylate (NaPA) solutions in the ultrasonic (US) field has been studied. It was observed, that the yellow colloidal solutions of stabilized AgNPs with the absorption maximum at ∼ 410 nm were obtained under the application of US power by 20 W and frequency by 20 kHz in the wide range of AgNO₃ and NaPA concentrations (0.1 - 0.5 mM and 0.5 - 5.0 g/L respectively) at 25 ⁰C. It was shown, that the GR process under US field occurs without of the significant induction period. Using the UV-vis spectroscopy the kinetics of AgNPs formation has been studied and it was observed the first order kinetics with respect to Ag⁺ ions both for the nucleation and growth processes. It was found that observable rate constants of nucleation are close for the all experimental conditions but the observable rate constants of growth decreased with increasing of initial concentration of AgNO₃. Based on the obtained kinetic data it was proposed a mechanism of the formation of AgNPs consisted of the following two main stages: 1) the nucleation with the formation of primary nanoclusters (AgNCs) on aluminum surface followed by their ablation from the surface of the sacrificial metal by ultrasound into bulk of solution; 2) the transformation of AgNCs in AgNPs via growth from the Al surface and / or agglomeration of AgNCs. Using TEM it was found that the size of obtained AgNPs does not exceed of 25 nm and slightly depends on the initial concentrations of precursors. High antimicrobial activity of obtained colloidal solutions against gram-negative and gram-positive bacteria as well as against fungi was observed.