Development and Characterization of Silver-Doped Multi-Walled Carbon Nanotube Membranes for Water Purification
Muhammad Umar Amjad1, Bilal Anjum Ahmed1, Faisal Ahmed1
1Department of Mechanical Engineering (CEME), National University of Sciences and Technology (NUST), Sector H-12, Islamabad 4600, Pakistan.
Abstract:
A unique approach was utilized to develop multi-walled carbon nanotube (MWCNT) silver (Ag) membranes. MWCNTs were impregnated with 1 wt% Ag loading, which resulted in a homogeneous dispersion of Ag in MWCNTs. MWCNTs impregnated with Ag were then uniaxially compacted at two different pressures of 80 MPa and 120 MPa to form a compact membrane. Compacted membranes were then sintered at two different temperatures of 800 °C and 900 °C to bind Ag particles with MWCNTs as Ag particles also act as a welding agent for CNTs. The powder mixture was characterized by FESEM, thermogravimetric analysis, and XRD, while the developed samples were characterized by calculating the porosity of membrane samples, contact angle, water flux and a diametral compression test. The developed membranes showed overall large water flux, while maximum porosity was found to decrease as the compaction load and sintering temperature increased. The mechanical strength of the membranes was found to increase as the compaction load increased. The hydrophilicity of the membranes remained unchanged after the addition of Ag particles. The developed membranes would be useful for removing a variety of contaminants from water.
More Related Videos
09:12Functionalization of Single-walled Carbon Nanotubes with Thermo-reversible Block Copolymers and Characterization by Small-angle Neutron Scattering
Published on: June 1, 2016
12:47Preparation and Use of Photocatalytically Active Segmented Ag|ZnO and Coaxial TiO2-Ag Nanowires Made by Templated Electrodeposition
Published on: May 2, 2014