Performance of PVDF-TiO₂ Membranes during Photo-Filtration in the Presence of Inorganic and Organic Components

In this study, the anti-fouling performance of PVDF-TiO₂ composite membranes, indicated by their permeate flux, was studied with different types of synthetic feed solutions. Photo-filtration (filtration under continuous UV irradiation) of solutions containing inorganic and organic components, which are ubiquitous in drinking/natural water, was performed to evaluate their influence on the photo-induced properties and performance of the membranes. The results indicated that inorganic fouling was unlikely to occur on PVDF-TiO₂ membranes, and the presence of common inorganic ions in drinking water did not hinder their performance. However, in the particular case where a small amount of Cu²⁺ coexisted alongside HCO₃^- in the feed solution, inorganic fouling occurred, causing severe flux decline and prohibiting the photo-induced properties of the membranes. On the other hand, when used to filter organic fouling solutions, the membranes showed strong resistance to sodium alginate fouling, and less so for humic acids. In terms of separation efficiency, the membranes showed no advantages when operated in photo-filtration mode, as the rejection rate of both foulants under photo-filtration was not higher than that under normal filtration. In the case of humic acids, the photodegradation of humic substances into smaller compounds that were able to enter the permeate stream led to a lower rejection rate. Nevertheless, photo-filtration of these organic foulants still offered a higher permeate flux than normal filtration, up to a certain concentration level (5 mg/L for humic acids and 50 mg/L for sodium alginate).