Influence of Bi₂O₃ on Mechanical Properties and Radiation-Shielding Performance of Lithium Zinc Bismuth Silicate...

We analyzed the mechanical properties and radiation-shielding performance of a lithium zinc bismuth silicate glass system. The composition of these glasses is 20ZnO-30Li₂O-(50-x)SiO₂-xBi₂O₃ (x varies between 10 and 40 mol%). The mechanical properties of the investigated glass system, such as Young's modulus (E), bulk modulus (K), shear modulus (S), and longitudinal modulus (L), were determined using the Makishima-Mackenzie model. The elastic moduli gradually decreased with the addition of Bi₂O₃. E decreased from 46 to 31 GPa, K decreased from 27 to 14 GPa, S decreased from 19 to 14 GPa, and L decreased from 52 to 32 GPa as Bi₂O₃ was substituted for SiO₂. The mass attenuation coefficient (MAC) was investigated at energies between 0.284 and 1.33 MeV to understand the radiation-shielding performance of the glasses. The MAC value increased when SiO₂ was replaced by Bi₂O₃. We found that the effect of Bi₂O₃ on MAC values was noticeably stronger at energies of 0.284 and 0.347 MeV, while the effect of Bi₂O₃ on MAC values became weaker as energy increased. The linear attenuation coefficient (LAC) results demonstrated that if the samples were exposed to low-energy photons, the glass could prevent the penetration of photons, and thus, the glass samples were effective in radiation protection. The LAC values for the lowest- and highest-density samples changed from 0.998 to 1.976 cm^-1 (at 0.284 MeV) and from 0.286 to 0.424 cm^-1 (at 0.826 MeV). According to the radiation-shielding results, the thick, high-density glass sample has special and distinctive shielding properties.