Experimental and Numerical Study on the Failure Characteristics of Brittle Solids with a Circular Hole and Internal

Chengjun Le1,2, Xuhua Ren1, Haijun Wang3

  • 1College of Water Conservancy and Hydropower Engineering, Hohai University, Nanjing 210098, China.

Materials (Basel, Switzerland)
|February 25, 2022
PubMed

Keywords:
3D internal crack3D-ILCbrittle solidscrack propagationfracture mechanicsproblem with circular hole

More Related Videos

Performing Microscope-Mounted Y-Shaped Cutting Tests06:15

Performing Microscope-Mounted Y-Shaped Cutting Tests

Published on: January 20, 2023

2.0K
Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture09:53

Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture

Published on: May 13, 2018

8.4K

Related Concept Videos

Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
2.9K
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
272
Plastic Deformation in Circular Shafts01:20

Plastic Deformation in Circular Shafts

When materials are subjected to forces that surpass their yield strength, they undergo a process known as plastic deformation. This results in a permanent alteration or strain in their structure. This concept can be specifically applied to circular shafts, where the deformation leads to a change in its shape. The precise evaluation of this plastic deformation requires understanding the stress distribution within the circular shaft, which is achieved by calculating the maximum shearing stress in...
267
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
306
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
223
Thin-Walled Hollow Shafts01:15

Thin-Walled Hollow Shafts

In analyzing a thin-walled hollow shaft subjected to torsional loading, a segment with width dx is isolated for examination. Despite its equilibrium state, this segment faces torsional shearing forces at its ends. These forces are quantitatively described by the product of the longitudinal shearing stress on the segment's minor surface and the area of this surface, leading to the concept of shear flow. This shear flow is consistent throughout the structure, indicating a uniform distribution...
277