Sintering Nano-Silver Paste by Resistive Joule Heating Process for 2G HTS Tape Joints

Developing a joining technology for 2G HTS tapes without significantly reducing their superconducting property is crucial for numerous applications (MRI, motor/generator, power transmission, etc.). In this study, low sintering temperature (~230 °C) nano-silver paste was used as solder to join two 2G HTS tapes. In addition, two heating methods, i.e., furnace heating (heat flux outside-in) and resistive Joule heating (heat flux inside-out), were studied. This study indicates that the heat flux from internal by resistive Joule heating method shows less deteriorating impact to the 2G RE-Ba-Cu-O tape (RE: rare earth element) during the sintering process with the best specific resistance of 0.074 μΩ∙cm² and I retention percentage of 99% (i.e., I reduced from 100 A before joining to 99 A after joining). This study indicates that nano-silver paste together with resistive Joule heating can possibly be used as soldering materials to join 2G HTS tapes.