Long-Term Potentiodynamic Testing and Tribometric Properties of Amorphous Alloy Coatings under Saline Environment

Protective coatings for harsh environments are always welcome, but they must overcome profound challenges, including corrosion and wear resistance. The purpose of this study is to look into the long-term potentiodynamic polarization measurements and dry tribometric behavior of plasma-sprayed amorphous coatings on AISI 1035 mild steel. To investigate the impact of unique active polarization potentials on the electrochemical studies of the iron-based amorphous layer, which compares favorably to AISI 1035 mild steel, the active potential polarization curve and friction coefficient tests were performed. Scanning electron microscopy (SEM) and energy dispersive x-ray (EDX) analyses were used to investigate the coating's corrosion behavior. Their mechanical (Tribometric tests at higher sliding speeds) and chemical properties (electrochemical potentiodynamic polarization investigations) have also been thoroughly investigated. There is enough validation that these protective coatings can be used in hostile environments. The effects of long-term corrosion for 24 and 48 h were thoroughly examined. Tribometric examinations revealed that amorphous layers are highly resistant under dry conditions, as they offered a very low and stable friction coefficient less than 4 μ with micro Vickers hardness 1140 ± 22.14 HV, which is more than twice as compared to mild steel AISI 1035. The corrosion resistance of coatings in 3.5 wt % NaCl solution displays active transition characteristics of activation, passivation, over passivation, and pitting, as shown by the potentiodynamic polarization curves.