A facial strategy to efficiently improve catalytic performance of CoFe₂O₄ to peroxymonosulfate

Cobalt iron spinel (CoFe₂O₄) has been considered as a good heterogeneous catalysis to peroxymonosulfate (PMS) in the degradation of persistent organic pollutants due to its magnetic properties and good chemical stability. However, its catalytic activity needs to be further improved. Here, a facial strategy, "in-situ substitution", was adopted to modify CoFe₂O₄ to improve its catalytic performance just by suitably increasing the Co/Fe ratio in synthesis process. Compared with CoFe₂O₄, the newly synthesized Co_1.5Fe_1.5O₄, could not only significantly improve the degradation efficiency of phenol, from 50.69 to 93.6%, but also exhibited more effective mineralization ability and higher PMS utilization. The activation energy advantage for phenol degradation using Co_1.5Fe_1.5O₄ was only 44.2 kJ/mol, much lower than that with CoFe₂O₄ (127.3 kJ/mol). A series of related representations of CoFe₂O₄ and Co_1.5Fe_1.5O₄ were compared to explore the possible reasons for the outstanding catalytic activity of Co_1.5Fe_1.5O₄. Results showed that Co_1.5Fe_1.5O₄ as well represented spinel crystal as CoFe₂O₄ and the excess cobalt just partially replaced the position of iron without changing the original structure. Co_1.5Fe_1.5O₄ had smaller particle size (8.7 nm), larger specific surface area (126.3 m²/g), which was more favorable for exposure of active sites. Apart from the superior physical properties, more importantly, more reactive centers Co (Ⅱ) and surface hydroxyl compounds generated on Co_1.5Fe_1.5O₄, which might be the major reason. Furthermore, Co_1.5Fe_1.5O₄ behaved good paramagnetism, wide range of pH suitability and strong resistance to salt interference, making it a new prospect in environmental application.