Cation-doping strategies for tuning of zirconia acid-base properties

The role of Y-, Ca- and Ce-doping of cubic zirconia (c-ZrO₂) (111) surface on its acidity, basicity and the interplay between surface acid-base pairs is investigated by computational methods. The most stable surface structures for this investigation were initially determined based on previous studies of Y-doped c-ZrO₂ (111) and by a detailed exploration of the most stable configuration for Ca-doped c-ZrO₂ (111) and Ce-doped c-ZrO₂ (111). Next, surface mapping by basic probe molecules (NH₃ and pyridine) revealed a general reduction of the acidity of the surface sites, although a few exceptions were observed for zirconium ions at next nearest neighbour (NNN) positions to the oxygen vacancy and at the nearest neighbour (NN) position to the dopants. Adsorption of CO₂ over basic sites revealed a cooperative interplay between acid-base groups. In this case, the overall effect observed was the decrease of the calculated adsorption energies when compared with the pristine surface. Moreover, spontaneous formation of η ³-CO₂ systems from initial η ²-CO₂ configurations indicates a decrease in the required energy for forming oxygen vacancies in the doped ZrO₂ systems at NNN positions or further away from the existing vacancy site.