Effect of Printing Layer Thickness and Postprinting Conditions on the Flexural Strength and Hardness of a 3D-Printed
Abdullah A Alshamrani1,2, Raju Raju3, Ayman Ellakwa1
1Oral Rehabilitation & Dental Biomaterial and Bioengineering, Sydney Dental School, Faculty of Medicine and Health, The University of Sydney, Australia.
Background:
Recently, dentists can utilize three-dimensional printing technology in fabricating dental restoration. However, to date, there is a lack of evidence regarding the effect of printing layer thicknesses and postprinting on the mechanical properties of the 3D-printed temporary restorations with the additive manufacturing technique. So, this study evaluated the mechanical properties of a 3D-printed dental resin material with different printing layer thicknesses and postprinting methods.
Methods:
210 specimens of a temporary crown material (A2 EVERES TEMPORARY, SISMA, Italy) were 3D-printed with different printing layer thicknesses (25, 50, and 100 μm). Then, specimens were 3D-printed using DLP technology (EVERES ZERO, DLP 3D printer, SISMA, Italy) which received seven different treatment conditions after printing: water storage for 24 h or 1 month, light curing or heat curing for 5 or 15 minutes, and control. Flexural properties were evaluated using a three-point bending test on a universal testing machine (ISO standard 4049). The Vickers hardness test was used to evaluate the microhardness of the material system. The degree of conversion was measured using an FT-IR ATR spectrophotometer. Statistical analysis was performed using two-way analysis of variance (ANOVA) and Tukey's honestly significant difference (HSD) test (p ≤ 0.05).
Results:
The 100 μm printing layer thickness had the highest flexural strength among the other thickness groups. As a combined effect printing thickness and postprinting conditions, the 100 μm with the dry storage group has the highest flexural strength among the tested groups (94.60 MPa). Thus, the group with 100 μm thickness that was heat cured for 5 minutes (HC 5 min 100 μm) has the highest VHN value (VHN = 17.95). Also, the highest mean DC% was reported by 50 μm layer thickness (42.84%).
Conclusions:
The thickness of the 100 μm printing layer had the highest flexural strength compared to the 25 μm and 50 μm groups. Also, the postprinting treatment conditions influenced the flexural strength and hardness of the 3D-printed resin material.
More Related Videos
03:02Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
Published on: January 17, 2025
07:283D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization
Published on: February 18, 2022