Mechanical performance of graphene_x/poly(ether ketone ketone) composite sheets by hot pressing

Polymer composites are gradually replacing traditional metal materials in the fields of aviation, aerospace, automotive and medicine due to their corrosion resistance, light weight and high strength. Moulding technology and organization morphology of polymer composite are key elements affecting the quality of products and their application, so a vacuum hot pressing process for graphene_x/poly(ether ketone ketone) (PEKK) (x = 0%, 2%, 3%, 4%, 5%, 6%) composite powders is explored with particularly designed moulding parameters to achieve high conductive properties and good mechanical properties in graphene/PEKK composite sheet with thickness of 1.25 mm and diameter of 80 mm. The vacuum environment ensures that the graphene is not oxidized by air during hot pressing molding, which is essential for achieving conductive property in the graphene/PEKK composite; The hot pressing temperature of each graphene/PEKK composite powder is higher than glass transition temperature but lower than melting temperature, which ensures the graphene/PEKK composite powders is fully compacted and then graphene is fully lapped in the composite sheet. In addition, the graphene/PEKK composite sheet shows conductive property when the graphene content increases to 3wt%, and then the conductivity of the composites increases and then decreases with a peak value at 5wt% with increasing graphene content. By comparing the mechanical properties and microstructure morphology of the graphene/PEKK composite sheets, it was obtained that graphene content has an obvious effect on the mechanical properties of the composites, e.g., the mechanical properties will be increased as the graphene content increasing when graphene content is more than 3%. The graphene distribution law of the composite material with different graphene contents is analysed using a scanning electron microscope (SEM).