The Structural Integrity and Fracture Behaviour of Teeth Restored with PEEK and Lithium-Disilicate Glass Ceramic...

Polyetheretherketone (PEEK) is a unique polymer material which has recently been introduced to dentistry. This study aimed to assess the structural integrity of PEEK as a posterior tooth crown and compared it with ceramic-based material. A total of 31 monolithic CAD-CAM PEEK (JuvoraTM, Strumann, Andover, MA, USA) crowns and 31 lithium disilicate (IPS e.max®CAD, Voclar Vivadent AG, Liechtenstein) crowns were created and cemented on dentin-like teeth (AlphaDie®MF, Schütz Dental GmbH, Rosbach, Germany) in a precise procedure mimicking the physical and mechanical properties of natural teeth and periodontal ligaments. A static compressive strength test using a universal testing machine and a dynamic fatigue test using a chewing simulator machine were used until crown failure to assess the fracture behaviour by mode of fracture (fractographic analysis) and 3D digital subtraction analysis. The results showed that PEEK has a greater fracture resistance than IPS e.max®CAD by 2060 N to 703 N. Additionally, in fatigue limit, IPS e.max®CAD showed a constant failure under 2.0 Kg (=320 N) before 5000 chewing cycles while PEEK survived at a significantly higher load > 11 Kg (930 N). Furthermore, PEEK showed a continued survival at >1,250,000 cycles while the mean fatigue life of IPS e.max®CAD was around 133,470 cycles. PEEK illustrated a significantly less catastrophic failure mode with some plastic deformation at the fractographic stereomicroscope and in the 3D digital subtraction analysis. Using PEEK for crowns looks very promising, however, further clinical studies are required to assure this study’s results.