Thermal Change Affects Flexural and Thermal Properties of Fused Deposition Modeling Poly(Lactic Acid) and Compression
Taksid Charasseangpaisarn1,2, Chairat Wiwatwarrapan1,3, Viritpon Srimaneepong4
1Dental Biomaterials Science, Graduate School, Chulalongkorn University, Bangkok, Thailand.
Objective:
Polylactic acid (PLA) is one of the most widely used materials in three-dimensional (3D) printing technology due to its multiple advantages such as biocompatibility and biodegradable. However, there is still a lack of study on 3D printing PLA for use as a denture base material. The goal of this study was to compare 3D printing PLA to traditional poly(methyl methacrylate) (PMMA) as a denture basis.
Materials And Methods:
The PMMA (M) and PLA (L) specimens were fabricated by compression molding, and fuse deposition modeling technique, respectively. Each specimen group was divided into three different temperature groups of 25°C (25), 37°C (37), and 55°C (55). The glass transition temperature (Tg) of raw materials and specimen was investigated using differential scanning calorimetry. The heat deflection temperature (HDT) of each material was also observed.
Statistical Analysis:
The data of flexural strength and flexural modulus were analyzed with two-way analysis of variance, and Tukey honestly significant difference. The Tg and HDT data, on the other hand, were descriptively analyzed.
Results:
The results showed that PLA had lower flexural strength than PMMA in all temperature conditions, while the PMMA 25°C (M25) and PMMA 37°C (M37) obtained the highest mean values. PLA 25°C (L25) and PLA 37°C (L37) had significant higher flexural modulus than the other groups. However, the flexural properties of L55 could not be observed, which may be explained by Tg and HDT of PLA.
Conclusion:
PLA only meets the flexural modulus requirement, although it was greater than flexural modulus of PMMA. On the other hand, PMMA can meet both good flexural strength and modulus requirement. However, increase in temperature could reduce flexural strength and flexural modulus of PMMA and PLA.
Related Concept Videos
01:26Polymer Classification: Stereospecificity
01:21Polymer Classification: Crystallinity
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
01:14Polymer Classification: Architecture
01:08Molecular Weight of Step-Growth Polymers
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
01:20Types of Step-Growth Polymers: Polyesters
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the...
01:12Temperature Dependent Deformation