Optimized hot electron injection from Cu nanoparticles to S-doped C₃N₄ by the formed S-Cu bonds for an enhanced...

Low-cost and high-abundance Cu nanostructures are potential near-infrared (NIR) surface plasmonic resonance (SPR) photosensitizers for carbon nitride (C₃N₄) photocatalysts, but their low activity and stability need to be improved. In this article, doping S into C₃N₄ (S-C₃N₄) creates anchoring sites for photo-deposited Cu nanoparticles (NPs), and the spontaneous construction of S-Cu bonds is realized between S-C₃N₄ and Cu NPs. The optimal hydrogen evolution rate of 1.64 mmol g^-1 h^-1 is obtained for S-C₃N₄-Cu, which is 5.5, 4.6 and 1.7 times that of pure C₃N₄, S-C₃N₄ and S-C₃N₄-Cu, respectively. With further loading of a Pt co-catalyst to confirm the role of Cu NPs and improve the photocatalytic activity of the SCN-Cu, the photocatalytic rate can reach up to 14.34 mmol g^-1 h^-1. Due to the NIR SPR effect of Cu NPs, the apparent quantum efficiency (AQE) of S-C₃N₄-Cu at 600 and 765 nm is 2.02% and 0.47%, respectively. The enhanced photocatalytic performance of S-C₃N₄-Cu compared with C₃N₄-Cu is mainly due to the introduced S-Cu bonds that improve the injection rate of hot electrons. This solution provides a simple and efficient interface optimization strategy for the construction of efficient NIR-driven photocatalysts.