Effects of Air Entrainment on Bacterial Viability in Cement Paste

This study investigated the effect of air entrainment (AE) on bacterial viability in cementitious materials. Specimens were fabricated with Portland cement, urea, calcium lactate, and ureolytic bacteria, and with varying amounts of an AE agent. Specimens with different amounts of the AE agent were fabricated, and then a compressive strength test, quantitative polymerase chain reaction, X-ray diffraction, and thermogravimetry were used to investigate the mechanical properties, viability of bacteria, and hydrates of the specimens. The highest compressive strength was achieved by the specimen with 0.3% AE agent, while the compressive strength of the specimens decreased considerably when the incorporated AE agent was over 0.6%, due to increased porosity. The quantitative polymerase chain reaction result showed that the cell number of the viable bacteria was increased by incorporation of the AE agent, which also corresponded with an increase in CaCO₃ due to microbial mineral formation. The obtained result confirmed the positive effect of AE agent incorporation in cementitious materials containing bacterial admixtures, as the viability of bacteria, which play a vital role in self-healing efficiency of concrete, was increased by the space provided by the AE agent in the cement matrix. In addition, the quantity of CaCO₃ and the compressive strength were highest when 0.3% AE agent was incorporated.