CVD-Synthesis of N-CNT Using Propane and Ammonia

N-CNT is a promising material for various applications, including catalysis, electronics, etc., whose widespread use is limited by the significant cost of production. CVD-synthesis using a propane-ammonia mixture is one of the cost-effective processes for obtaining carbon nanomaterials. In this work, the CVD-synthesis of N-CNT was conducted in a traditional bed reactor using catalyst: (Al_0,4Fe_0,48Co_0,12)₂O₃ + 3% MoO₃. The synthesized material was characterized by XPS spectroscopy, ASAP, TEM and SEM-microscopy. It is shown that the carbon material contains various morphological structures, including multiwalled carbon nanotubes (MWCNT), bamboo-like structures, spherical and irregular sections. The content of structures (bamboo-like and spherical structure) caused by the incorporation of nitrogen into the carbon nanotube structure depends on the synthesis temperature and the ammonia content in the reaction mixture. The optimal conditions for CVD-synthesis were determined: the temperature range (650-700 °C), the composition (C₃H₈/NH₃ = 50/50%) and flow rate of the ammonia-propane mixture (200 mL/min).