Influence of Monocalcium Phosphate on the Properties of Bioactive Magnesium Phosphate Bone Cement for Bone...

Bone defects occurring for various reasons can lead to deformities and dysfunctions of the human body. Considering the need for clinical applications, it is essential for bone regeneration to exploit a scaffold with bioactive bone cement. In this study, we fabricated bioactive magnesium phosphate bone cement (BMPC) at room temperature; then, it was set at to °C and 100% humidity for 2 h. The process was as follows: Simulating a clinical environment, magnesium oxide (MgO) was formed by calcining basic magnesium carbonate (Mg₂(OH)₂CO₃). MgO, potassium dihydrogen phosphate (KH₂PO₄) and carboxymethyl chitosan (C₂₀H₃₇N₃O₁₄, CMC) were mixed to form magnesium phosphate bone cement (MPC); then, monocalcium phosphate (Ca(H₂PO₄)₂) was added to neutralize the alkaline product after MPC hydration to fabricate bioactive magnesium phosphate bone cement (BMPC). The influence of the doped content of Ca(H₂PO₄)₂ on the properties of bone cement was discussed. The results showed that Ca(H₂PO₄)₂ and CMC can adjust the setting time of bone cement to between 8 and 25 min. The compressive strength increased first and then decreased. After 48 h without additional pressure, the compressive strength reached the maximum value, which was about 38.6 MPa. Ca(H₂PO₄)₂ and CMC can play a synergistic role in regulating the properties of BMPC. The BMPC was degradable in the simulated body fluid (SBF). The results of the cytotoxicity experiment and laser confocal microscopy experiment indicated that BMPC fabricated at room temperature had better biocompatibility and degradability, which was more consistent with clinical operation requirements. BMPC is a promising orthopedic material and is suitable for repairing bone defects.