Effect of Active Bonding Application after Selective Dentin Etching on the Immediate and Long-Term Bond Strength of...

The objective was to evaluate the influence of active bonding applications (ABA) for different time intervals after selective dentin etching (SDE) for 3 s on the microtensile bond strength (μTBS) to dentin of two universal adhesive systems (UAs): one containing 2-hydroxyethyl methacrylate (HEMA) (Scotchbond Universal, SBU), and one that was HEMA-free (Prime&Bond Universal, PBU). Dentin bovine specimens were divided into four groups: self-etch as control (SE), SDE + ABA for 15 s (SDE15), SDE + ABA for 20 s (SDE20), and SDE + ABA for 25 s (SDE25). The μTBS test was performed after a water storage of 24 h and 6 months. Scanning electron microscopy (SEM) was used in order to examine the resin−dentin interface. For the PBU, the µTBS was significantly influenced only by the aging factor (p < 0.026). A statistically significant decrease in the µTBS after 6 months of aging was observed only for the SDE15 group. For SBU, µTBS was significantly influenced by the protocol application and the aging time (p ≤ 0.041). The groups SDE15, SDE20, and SDE25 achieved statistically significant higher values (after 24 h and 6 months). No considerable variances were noticed in the homogeneity and continuity of the hybrid layer (HL) among the groups. In conclusion, SDE and ABA improved the µTBS only of a HEMA-containing universal adhesive.