Preparation of Functional Silica Using a Bioinspired Method
Published on: August 1, 2018
One-Pot Synthesis of Amine-Functionalized Nano-Silica via Sol-Gel Assisted by Reverse Micelle Microemulsion for
Enshirah Da'na1, Wafa Shamsan Al-Arjan2, Sukainah Al-Saeed2
1Biomedical Engineering Department, College of Engineering, King Faisal University, P.O. Box 400, Al-Ahsa 31982, Saudi Arabia.
Abstract:
Amine modified nano-silica was prepared via a one-pot route and under very mild conditions in water in oil microemulsion with a non-ionic surfactant to study the effect of changing the amount of N-[3-(Trimethoxysilyl)propyl]ethylenediamine (DA) added to the synthesis mixture on the characteristics of the obtained nanocomposite such as morphology, crystallinity, surface charge, particle size, surface area, and accordingly the effect of all of these factors on the efficiency of the nanocomposite for the removal of heavy metal ions, namely zinc, from aqueous solutions. XRD, SEM, TGA, BET, DLS, FTIR, and pH0 analysis were performed for samples and the results showed a strong effect for the amount of DA added to the synthesis mixture on the characteristics of the obtained nanocomposites. It was found that increasing the amount of DA added to the synthesis mixture increased the pH0, hydrodynamic particle size obtained by dynamic light scattering analysis, and the particle size obtained by SEM. Sample prepared without the addition of DA (SNP) and the samples prepared with 1.5 mL of DA (SNP-1.5DA) showed a better adsorption performance compared to the samples prepared with 0.5 and 1.0 mL of DA (SNP-0.5DA and SNP-1.0DA, respectively). The main factor affecting the adsorption efficiency was found to be the available surface area for each nanocomposite, which was directly related to the degree of crystallinity as obtained by XRD analysis.