Modulation of Hierarchical Pores in Metal-Organic Frameworks for Improved Dye Adsorption and Electrocatalytic...

The hierarchical porous metal-organic framework (HP-MOF) has emerged as a hot topic in porous materials in consideration of their advantages in storage capacity and catalysis performance. Herein, we report the construction and property investigation of a series of HP-MOFs. A series of isoreticular microporous MOFs featuring the pacs topology network based on 2,4,6-tris(4-pyridyl)-1,3,5-triazine and different carboxylic acid ligands are found to be potential precursors to construct HP-MOFs. Through the decarboxylation of carboxylate ligands at high temperatures, a hierarchical porous structure could be obtained with the reservation of a crystalline framework. The formation of hierarchical pores is highly dependent on the structural and component nature (carboxylate ligands and metal centers) of the pristine MOF and the pyrolysis conditions (temperature and treatment time), indicating the highly tunable hierarchical pore characteristic of the HP-MOFs. By taking advantage of the increased pore volume and more exposed activation sites, the HP-MOFs reveal enhanced anionic dye adsorption capacity (800 mg·g^-1 for Congo red and 140 mg·g^-1 for methyl blue) and catalytic activity toward electrocatalytic oxygen reduction reaction (overpotential of 0.302 V at a current density of 10 mA·cm^-2, 51 mV lower than that of the pristine MOF).