Emulsion Templated Porous Poly(thiol-enes): Influence of Photopolymerisation, Emulsion Composition, and Phase...

1,6-hexanediol diacrylate (HDDA) or divinyl adipate (DVA) and pentaerythritol tetrakis(3-mercaptopropionate) (TT) were polymerised via a thiol-ene radical initiated photopolymerisation using emulsions with a high volume fraction of internal droplet phase and monomers in the continuous phase as precursors. The porous structure derived from the high internal phase emulsions (HIPEs) followed the precursor emulsion setup resulting in an open porous cellularly structured polymer. Changing the emulsion composition and polymerisation conditions influenced the resulting morphological structure significantly. The investigated factors influencing the polymer monolith morphology were the emulsion phase ratio and surfactant concentration, leading to either interconnected cellular type morphology, bicontinuous porous morphology or a hollow sphere inverted structure of the polymerised monoliths. The samples with interconnected cellular morphology had pore diameters between 4 µm and 10 µm with approx. 1 µm sized interconnecting channels while samples with bicontinuous morphology featured approx. 5 µm wide pores between the polymer domains. The appropriate choice of emulsion composition enabled the preparation of highly porous poly(thiol-enes) with either polyHIPE or bicontinuous morphology. The porosities of the prepared samples followed the emulsion droplet phase share and could reach up to 88%.