Tensile Strength Essay Comparing Three Different Platelet-Rich Fibrin Membranes (L-PRF, A-PRF, and A-PRF+): A...

Predictable outcomes intended by the application of PRF (platelet-rich fibrin) derivative membranes have created a lack of consideration for their consistency and functional integrity. This study aimed to compare the mechanical properties through tensile strength and analyze the structural organization among the membranes produced by L-PRF (leukocyte platelet-rich fibrin), A-PRF (advanced platelet-rich fibrin), and A-PRF+ (advanced platelet-rich fibrin plus) (original protocols) that varied in centrifugation speed and time. L-PRF (n = 12), A-PRF (n = 19), and A-PRF+ (n = 13) membranes were submitted to a traction test, evaluating the maximum and average traction. For maximum traction, 0.0020, 0.0022, and 0.0010 N·mm−2 were obtained for A-PRF, A-PRF+, and L-PRF, respectively; regarding the average resistance to traction, 0.0012, 0.0015, and 0.006 N·mm−2 were obtained, respectively (A-PRF+ > A-PRF > L-PRF). For all groups studied, significant results were found. In the surface morphology observations through SEM, the L-PRF matrix showed a highly compact surface with thick fibers present within interfibrous areas with the apparent destruction of red blood cells and leukocytes. The A-PRF protocol showed a dense matrix composed of thin and elongated fibers that seemed to follow a preferential and orientated direction in which the platelets were well-adhered. Porosity was also evident with a large diameter of the interfibrous spaces whereas A-PRF+ was the most porous platelet concentrate with the greatest fiber abundance and cell preservation. Thus, this study concluded that A-PRF+ produced membranes with significant and higher maximum traction results, indicating a better viscoelastic strength when stretched by two opposing forces.