Processing, Characterization of Furcraea foetida (FF) Fiber and Investigation of Physical/Mechanical Properties of...

In recent days the rising concern over environmental pollution with excessive use of synthetic materials has led to various eco-friendly innovations. Due to the organic nature, abundance and higher strength, natural fibers are gaining a lot of interest among researchers and are also extensively used by various industries to produce ecological products. Natural fibers are widely used in the composite industry as an alternative to synthetic fibers for numerous applications and new sources of fiber are continuously being explored. In this study, a fiber extracted from the Furcraea foetida (FF) plant is characterized for its feasibility as a reinforcement to fabricate polymer composite. The results show that the fiber has a density of 0.903 ± 0.07 g/cm3, tensile strength (σt) of 170.47 ± 24.71 MPa and the fiber is thermally stable up to 250 °C. The chemical functional groups and elements present in the FF fiber are evaluated by conducting Fourier transform infrared spectroscopy (FT-IR) and energy dispersive spectroscopy (EDS). The addition of FF fibers in epoxy reduced the density (13.44%) and hardness (10.9%) of the FF/Epoxy (FF/E) composite. However, the void content (Vc < 8%) and water absorption (WA: < 6%) rate increased in the composite. The FF/E composite with 30% volume of FF fibers showed maximum σt (32.14 ± 5.54 MPa) and flexural strength (σf: 80.23 ± 11.3 MPa).