Corrosion Resistance of Selective Laser Melted Ti6Al4V3Cu Alloy Produced Using Pre-Alloyed and Mixed Powder

Metallic elemental powder mixture and pre-alloyed metallic powder are both frequently used powder feedstock in the additive manufacturing process. However, little research has been conducted to compare the corrosion behavior of selective laser melting (SLM) alloys, fabricated by pre-alloyed metallic powder and mixed metallic powder. Hence, it is important to investigate the corrosion behavior of SLMed alloys, as well as the corresponding cast ingot, with the aim to better understand the feasibility of designing new materials. In this work, the SLM-produced Ti6Al4V3Cu alloys were manufactured using a metallic elemental powder mixture and pre-alloyed metallic powder, respectively. The corrosion behavior of the different Ti6Al4V3Cu alloys was investigated in following electrochemical tests and ion release measurements. The results showed that the Ti6Al4V3Cu alloy prepared by pre-alloyed metallic powder showed better corrosion resistance than that produced from mixed metallic powder. Moreover, the SLM-produced Ti6Al4V3Cu alloys performed significantly better in corrosion resistance than the cast Ti6Al4V3Cu. The results are expected to achieve a better understanding of the feasibility of designing new materials using mixed powders, contributing to reducing development costs and cycles.