Investigation of the Initial Corrosion Destruction of a Metal Matrix around Different Non-Metallic Inclusions on

Elena Sidorova1,2, Andrey Karasev1, Denis Kuznetsov2

  • 1Department of Materials Science and Engineering, KTH Royal Institute of Technology, Brinellvägen 23, 100 44 Stockholm, Sweden.

Materials (Basel, Switzerland)
|April 12, 2022
PubMed

Keywords:
chemical extractioncorrosionelectrolytic extractionnon-metallic inclusionspipeline steels

More Related Videos

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation07:44

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation

Published on: March 15, 2017

15.9K
Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars10:24

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars

Published on: November 1, 2018

6.8K

Related Concept Videos

Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
276
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
25.7K
Deleterious Substances in Aggregate01:25

Deleterious Substances in Aggregate

Deleterious substances in aggregates can be detrimental to the quality and durability of concrete. These substances include organic impurities like loam, which interfere with cement hydration and are usually present in the sand. These prevent a good bond between aggregate and cement paste. Organic impurities can be detected using the colorimetric test, where the darkness of a solution after agitation indicates the level of organic content.
Another type of impurity is clay and fine material that...
277
Bending of Material: Problem Solving01:09

Bending of Material: Problem Solving

In this lesson, determine the ratio of the maximum bending moments applied to two metal pipes, given that both pipes can withstand a maximum stress of 100 MPa. Both pipes have an outer radius of 1.8 cm. Pipe A has an inner radius of 1.5 cm, and Pipe B has an inner radius of 1 cm. The ratio of the maximum bending moment applied to two metallic pipes, each with a different inner and outer radius, is determined by considering their dimensions. The inner radius of the first pipe is 1.5 cm, and for...
266