Nanoporous {Y₂}-Organic Frameworks for Excellent Catalytic Performance on the Cycloaddition Reaction of Epoxides with...

Stable metal-organic frameworks containing periodically arranged nanosized pores and active Lewis acid-base active sites are considered as ideal candidates for efficient heterogeneous catalysis. Herein, the exquisite combination of [Y₂(CO₂)₇(H₂O)₂] cluster (abbreviated as {Y₂}) and multifunctional linker of 2,4,6-tri(2,4-dicarboxyphenyl)pyridine (H₆TDP) led to a nanoporous framework of {[Y₂(TDP)(H₂O)₂]·5H₂O·4DMF} (NUC-53, NUC = North University of China), which is a rarely reported binuclear three-dimensional (3D) framework with hierarchical tetragonal-microporous (0.78 nm) and octagonal-nanoporous (1.75 nm) channels. The inner walls of these channels are aligned by {Y₂} clusters and plentifully coexisted Lewis acid-base sites of Y^III ions and N_pyridine atoms. Furthermore, NUC-53 has a quite large void volume of ∼65.2%, which is significantly higher than most documented 3D rare-earth-based MOFs. The performed catalytic experiments exhibited that activated NUC-53 showed a high catalytic activity on the cycloaddition reactions of CO₂ with styrene oxide under mild conditions with excellent turnover number (TON: 1980) and turnover frequency (TOF: 495 h^-1). Moreover, the deacetalization-Knoevenagel condensation reactions of benzaldehyde dimethyl acetal and malononitrile could be efficiently prompted by the heterogeneous catalyst of NUC-53. These findings not only pave the way for the construction of nanoporous MOF based on rare-earth clusters with a variety of catalytic activities but also provide some new insights into the catalytic mechanism.