Tunable LSPR of silver/gold bimetallic nanoframes and their SERS activity for methyl red detection

Ag/Au bimetallic nanostructures have received much attention in surface-enhanced Raman scattering (SERS). However, the synthesis of this nanostructure type still remains a challenge. In the present research, Ag/Au nanoframes were synthesized via a simple room temperature solution phase chemical reduction method using pre-synthesized triangular Ag nanoplates as templates in the presence of appropriate amounts of HAuCl₄. Controlling experimental parameters was applied for understanding of the growth mechanism. The galvanic exchange reaction resulted in a uniform deposition of the Au shell on the Ag nanoplates and the Ag core was removed which generated triangular hollow nanoframes. It is found that the amount of HAuCl₄ added to the growth solution played a key role in controlling the Ag/Au nanoframes. The resultant silver/gold nanoframes with average size of 50 nm were applied in detecting methyl red (MR) in the solution-phase using an excitation wavelength laser of 532 nm. The SERS signal was greatly enhanced owing to the tunable plasmonic peaks in the visible region (400-650 nm). The limit of detection (LOD) of MR in diluted solution was 10^-6 M. The enhancement factor (EF) was about 8 × 10⁴ toward 10^-5 M of MR. Interestingly, the linear dependence between the logarithm of the SERS signal intensity (log I) and the logarithm of the MR concentration (log C) occurred in the range from 10^-6 to 10^-4 M. Our work promises the application of Ag/Au nanoframes as a chemical sensor in detecting MR molecules at low concentration with high performance.