Accelerated bone regeneration through rational design of magnesium phosphate cements

Results of several studies during past years suggested that magnesium phosphate cements (MPCs) not only show excellent biocompatibility and osteoconductivity, but they also provide improved regeneration capacity due to higher solubility compared to calcium phosphates. These findings also highlighted that chemical similarity of bone substitutes to the natural bone tissue is not a determinant factor in the success of regenerative strategies. The aim of this study was to further improve the degradation speed of MPCs for a fast bone ingrowth within a few months. We confirmed our hypothesis, that decreasing the powder-liquid ratio (PLR) of cement results in an increased content of highly soluble phases such as struvite (MgNH₄PO₄⋅6H₂O) as well as K-struvite (MgKPO₄⋅6H₂O). Promising compositions with a low PLR of 1 g ml^-1 were implanted in partially-loaded tibia defects in sheep. Both cements were partially degraded and replaced by bone tissue after 4 months. The degradation speed of the K-struvite cement was significantly higher compared to the struvite cement, initially resulting in the formation of a cell-rich resorption zone at the surface of some implants, as determined by histology. Overall, both MPCs investigated in this study seem to be promising as an alternative to the clinically well-established, but slowly degrading calcium phosphate cements, depending on defect size and desired degradation rate. Whereas the K-struvite cement might require further modification towards a slower resorption and reduced inflammatory response in vivo, the struvite cement appears promising for the treatment of bone defects due to its continuous degradation with simultaneous new bone formation. STATEMENT OF SIGNIFICANCE: Cold setting bone cements are used for the treatment of bone defects that exceed a critical size and cannot heal on their own. They are applied pasty into the bone defect and harden afterwards so that the shape adapts to the individual defect. Magnesium phosphates such as magnesium ammonium phosphate hexahydrate (struvite) belong to a new class of these cold setting bone cements. They degrade much faster than the clinically established calcium phosphates. In this study, a magnesium phosphate that has hardly been investigated so far was implanted into partially-loaded defects in sheeps: Potassium magnesium phosphate hexahydrate. This showed even faster resorption compared to the struvite cement: after 4 months, 63% of the cement was already degraded.