Effect of Different Hot-Pressing Pressure and Temperature on the Performance of Titanium Mesh-Based MEA for DMFC

The hot-pressing process of the membrane electrode assembly (MEA) is one of the research hotspots in the field of the fuel cell. To obtain suitable titanium mesh-based MEA hot pressing process parameters, titanium mesh was used as electrode substrate material. The anode and cathode of MEA were prepared by the drip-coated method, and the titanium mesh-based MEA was prepared under different hot-pressing pressure and temperature, respectively. The performance of titanium mesh-based MEA was studied by morphological observation, elemental analysis, thickness measurement, single cell test and numerical fitting analysis. The results demonstrated that: with increasing hot-pressing pressure from 0 MPa to 10 MPa, the forming thickness of titanium mesh-based MEA is getting thin gradually, and the peak power density of titanium mesh-based MEA first increased and then gradually decreased; with increasing hot-pressing temperature from 115 °C to 155 °C, the peak power density of titanium mesh-based MEA enhanced at the beginning and then also gradually decreased. Under the premise of a hot-pressing time of 180 s and the optimal operating temperature of DMFC of 60 °C, the appropriate hot-pressing process conditions of titanium mesh-based MEA are a hot-pressing pressure of 5 MPa and a hot-pressing temperature of 135 °C. The results can provide a technological reference for the preparation of titanium mesh MEA for DMFC.