Discrete Element Modeling of Instability Mechanisms of Unbound Permeable Aggregate Base Materials in Triaxial...

Unbound permeable aggregate base (UPAB) materials with strong load-transmitting skeleton yet adequate inter-connected pores are desired for use in the sponge-city initiative. However, the micro-scale fabric evolution and instability mechanism of macroscopic strength behavior of such UPAB materials still remain unclear. In this study, virtual monotonic triaxial compression tests were conducted by using the discrete element method (DEM) modeling approach on specimens with different gradations quantified by the parameter of gravel-to-sand ratio (G/S). The realistic aggregate particle shape and inter-particle contact behavior were properly considered in the DEM model. The micromechanical mechanisms of the shearing failure of such UPAB materials and their evolution characteristics with G/S values were disclosed from contact force chains, microstructures, and particle motion. It was found that the proportion of rotating particles in the specimens decreased and the proportion of relative sliding between particles increased as the content of fine particles decreased. The plastic yielding of the specimens originated from the failure of contact force chains and the occurrence of the relative motion between particles, while the final instability was manifested by the large-scale relative motion among particles along the failure plane (i.e., changes in the internal particle topology). By comparing the macroscopic strength, microstructure evolution, and particle motion characteristics of the specimens with different G/S values, it was found that the specimens with G/S value of 1.8 performed the best, and that the G/S value of 1.8 could be regarded as the threshold for separating floating dense and skeletal gap type packing structures. The variation of Euler angles of rotating particles was significantly reduced in the particle size range of 4.75 mm to 9.50 mm, indicating that this size range separates most of the particles from rolling and sliding. Since particle rolling and sliding behavior are directly related to shear strength, this validates the rationality of the parameter G/S for controlling and optimizing gradations from the perspective of particle movement. The findings could provide theoretical basis and technical guidance for the effective design and efficient utilization of UPAB materials.