Study on Morphology and Chemical States of Surface Active Layer of Th-W Cathode

The surface morphology and chemical states of W-2%ThO₂ thermionic cathode during vacuum high-temperature treatment were investigated in this research. The W-2%ThO₂ thermionic cathode was prepared by a solid-liquid doping method combined with high-temperature sintering. The morphology and distribution of thorium oxide were observed using a transmission electron microscope and scanning electron microscope. The chemical states of elements at different temperatures were analyzed by X-ray photoelectron spectroscopy. Results indicate that the surface morphology and chemical form of the alloy evolve with the increase of temperature. The matrix had a lamellar structure at low temperatures, and the surface was relatively flat. The samples were heated to 500 °C, 1100 °C, and 1300 °C for 1 h. During the heating process, thorium oxide changed from granular to spherical, and the matrix was recrystallized. As the heating temperature rises, diffusion channels appear inside the cathode. As the temperature increases, the high-priced tungsten gradually decreases, and the zero-valent tungsten content increases. The adsorbed oxygen left the cathode surface, and the lattice oxygen increased. The surface oxygen content decreased, and the thorium and tungsten content increased.