Fluorine Effect for Improving Oxidation Resistance of Ti-45Al-8.5Nb Alloy at 1000 °C

In-depth analyses of the anti-oxidation behavior and structure of γ-TiAl alloys are of great significant for their maintenance and repair in engineering applications. In this work, fluorine-treated Ti-45Al-8.5Nb alloys and fluorine-treated oxidized specimens with artificial defects were prepared by isothermal oxidation treatment at 1000 °C. Several characterization methods, including SEM, EDS, XRD and TEM, were used to evaluate the surface microstructure of the fluorine-treated Ti-45Al-8.5Nb alloys and fluorine-treated oxidized specimens with artificial defects. The results indicate that the fluorine promoted the formation of an outer protective film of Al₂O₃, which significantly improved the oxidation resistance. The microcracks of oxidized specimens with the artificial defects provided a rapid diffusion passage for Ti and O elements during the 1000 °C/2 h isothermal oxidation treatment process, resulting in the quick growth of TiO₂ toward the outside. The fine Al₂O₃ constituted a continuous film after the 1000 °C/100 h isothermal oxidation treatment. In particular, Al₂O₃ particles grew toward the substrate, which was ascribed to the good oxidation resistance and adhesion. These results may provide an approach for the repair of protective oxide film on the surface of blades and turbine disks based on γ-TiAl alloys.