Mechanical Behavior of GFRP Laminates Exposed to Thermal and Moist Environmental Conditions: Experimental and Model...

This paper presents an experimental and analytical study about the mechanical response at a different temperature on glass fiber-reinforced polymer laminates. The effect of different environmental conditions on compressive, tensile, stiffness, and viscoelastic behavior (storage modulus, loss modulus and damping ratio) of laminates were investigated. Before testing, laminates were preserved in a deep freezer at -80 °C, -20 °C, 0 °C, and room temperature (25 °C) for up to 60 days. Results confirmed that temperatures ranging from -80 to 50 °C, which were below the glass transition temperature of the epoxy resin, did not significantly affect the compressive, tensile, and stiffness performance of all laminates. When the testing temperature increased to 100 °C, the properties were decreased significantly due to the damaging of the fiber/matrix interface. Additionally, results obtained from dynamic mechanical analyses tests showed a drop-in storage modulus, high peaks in loss modulus and high damping factor at the glass transition region of the epoxy resin. The highest storage modulus, two phases of glassy states and highest damping ratio on the -80/G group of laminates were obtained. The accuracy of experimental results was assessed with empirical models on the storage modulus behavior of laminates. The empirical model developed by Gibson et al. provided accurate estimates of the storage modulus as a function of temperature and frequency. The remaining empirical models were less accurate and non-conservative estimations of laminates stiffness.