Growth of Fe-BDC Metal-Organic Frameworks onto Functionalized Si (111) Surfaces

The realization of metal-organic framework (MOF) layers onto solid surfaces is a prerequisite for their integration into devices. This work reports the direct growth of Fe³⁺ /benzene di-carboxylate MOFs onto functionalized silicon surfaces, compatible with a wide range of MOF synthesis conditions. The co-nucleation and growth of different crystalline phases are evidenced, whose coverage depends on the surface chemistry and/or the solution composition. Three structural phases - the cubic MIL-101(Fe), a hexagonal phase with a structure close to MOF-235 and a MIL-53(Fe) with a monoclinic symmetry - are identified through characteristic crystal shapes and their structural parameters inferred from X-Ray Diffraction. In addition to the oriented growth of 3D crystallites, the formation of two-dimensional MIL-101 nano-crystallites or thin layers/islands exhibiting extended monocrystalline domains with (111) texture is also demonstrated through high-resolution atomic force microscopy. Post-synthesis treatments reveal a weak adhesion of the hexagonal phase, indicating a different surface anchoring.